Preparation and characterization of sputtered hydroxyapatite thin films

Thumbnail Image

Date

2018-01-19

Journal Title

Journal ISSN

Volume Title

Publisher

Pontificia Universidad Católica del Perú

Abstract

In this work, hydroxyapatite (HAp) thin films were fabricated using two different sputtering techniques: Radio frequency magnetron sputtering and ion beam sputtering. In the first case, the films were grown on Ti-6Al-4V substrates using a high-purity commercial HAp target, obtaining a thickness ~200 nm. For the second method, the film were grown on pure titanium substrates using a self-produced HAp target. This target was fabricated with powders (Ca/P = 1.628, sintered and crushed). Here, the thickness of the fabricated film was ~300 nm. The sintering tests for the target fabrication were carried out using two different heating regimens at a maximum temperature of 1200 °C (holding time of 2h and 4h) using various additives. As additives, water (H2O), polyvinyl alcohol (PVA) and polyethylene glycol (PEG) were used to improve the mechanical strength of the green discs. The as-deposited films were amorphous in both cases. Therefore, the films were annealed to increase the crystallinity. Annealing was performed in air for 2h at temperatures: 400, 600 and 800 °C for RF-magnetron sputter samples; 600 and 800 °C for ion beam sputter samples. The result of the films shows in both cases that the crystallinity of HAp was improved only for the annealed samples fabricated with ion beam sputtering at 800 °C. In both cases energy dispersive X-ray spectroscopy measurements show a decrease in Ca/P ratio with increasing the temperature. Hardness results revealed an increase in this with the increase in temperature possibly due to the formation of titanium oxide. The roughness for the fabricated films with the RFmagnetron sputtering increases till an annealing temperature of 600 °C and then decreases till 800 °C, while the roughness for the fabricated films with ion beam sputtering is higher in the as-deposited samples and then this is reduced by increasing the annealing temperature.

Description

Keywords

Hidrocarburos policíclicos aromáticos--Propiedades mecánicas, Películas delgadas

Citation

Endorsement

Review

Supplemented By

Referenced By

Creative Commons license

Except where otherwised noted, this item's license is described as info:eu-repo/semantics/openAccess